Friction and wear properties of Mo coatings on cast-iron substrates

Abstract

In order to protect machining parts against wear and corrosion in automotive, aerospace, pulp and paper industries, they are coated with Mo-based materials. For these specific applications, Mo coatings were fabricated on cast-iron substrates using an atmospheric plasma-spray system and their friction and wear behavior were evaluated. The Mo coatings were subjected to sliding wear against AISI 303 counter bodies under dry and acid environments. A pin-on-plate type of apparatus was used with normal loads of 49, 89 and 129 N, and sliding speed of 1 Hz. In the steady state, it was demonstrated that the Mo-coated samples under dry conditions had slightly higher wear resistance than under acid conditions tested under a load of 129 N. Several wear failure mechanisms, such as local plastic deformation, cracks, pits, debris, grooves, scratches and tracks, were identified after the tests. (C) 2003 Elsevier Science B.V. All rights reserved.