The selection of most proper materials in engineering design is known as an important stage of the design process. In order to successfully complete this stage, it is necessary to have sufficient knowledge about the structure ...
In the casting of liquid metal, the feeding stops when the mushy zone is clogged and does not allow the transfer of feeding liquid. The growing resistance of the solid dendrites against the fluidity of the feeding liquid ...
Barlas, Zafer; Çolak, Murat(PO BOX 197-IV, LJUBLJANA 61001, SLOVENIA, 2014)
Friction welding was applied to dissimilar aluminum cast bars alloyed with 2 and 8% copper and the effects of upset time on joint properties were evaluated in this study. The welding process was carried out by a vertical ...
The treatment of liquid aluminum prior to casting typically consists of purging gas and/or fluxes through the melt. By the use of several chemicals during these operations, several environmental problems can occur. Therefore, ...
Kayıkcı, Ramazan; Çolak, Murat; Şirin, Selçuk(INST ZA KOVINSKE MATERIALE I IN TEHNOLOGIE, 2015)
The results showed that the CFS values for solidifying aluminium alloys may vary from 34 % to 57 % depending on the casting conditions. The results also showed that for A356 aluminium-alloy castings the CFS value is not ...
The wear and friction performance of GUR 1020 grade ultrahigh molecular weight polyethylene (UHMWPE) polymer was studied in distilled water, HASS (Hank's balanced salt solution) and several protein lubrication environments. ...
The friction and wear properties of pure poly-tetra-fluoro-ethylene (PTFE), 35% carbon filled poly-tetra-fluoro-ethylene (PTFE+35%C), and 17% glass fiber-reinforced polytetra- fluoro-ethylene (PTFE+17% GFR) sliding against ...
In this study, the performance of boric acid (H3BO3)-filled polyamide composites were studied and evaluated at dry-sliding friction conditions. Wear tests were carried out using configuration of composite pin on a rotating ...