A study on NiAl produced by pressure-assisted combustion synthesis

Özdemir, Özkan; Zeytin, Sakin; Bindal, Cuma (PERGAMON-ELSEVIER SCIENCE LTD, 2009)

The production of intermetallic compound was carried out in an electrical resistance furnace in open air under 150 MPa uniaxial pressure at 1050 degrees C for 1 hour using aluminum powder with 15 mu m size and Carbonyl-nickel ...
Characterization of NiAl with cobalt produced by combustion synthesis

Özdemir, Özkan; Zeytin, Sakin; Bindal, Cuma (ELSEVIER SCIENCE SA, 2010)

In this study, as an alloying element the effect of cobalt addition by 2.5 wt.% and 5 wt.% on the NiAl intermetallic compound produced by pressure-assisted combustion synthesis method was investigated. As starting materials ...
Characterization of two-phase nickel aluminides produced by pressure-assisted combustion synthesis

Özdemir, Özkan; Zeytin, Sakin; Bindal, Cuma (PERGAMON-ELSEVIER SCIENCE LTD, 2007)

Two-phase (B2 + L1(2)) nickel aluminide intermetallic compounds were synthesized by the pressure-assisted volume combustion synthesis (CS). The production and characterization of the samples containing NiAl + Ni3Al were ...
Tribological properties of Ni3Al produced by pressure-assisted volume combustion synthesis

Özdemir, Özkan; Zeytin, Sakin; Bindal, Cuma (ELSEVIER SCI LTD, 2012)

The production of Ni3Al was performed under an uniaxial pressure of 150 MPa at 1050 degrees C for 1 h. The formation temperature of Ni3Al was determined to be 655 degrees C. The presence of Ni3Al was confirmed by XRD ...
Tribological properties of NiAl produced by pressure-assisted combustion synthesis

Özdemir, Özkan; Zeytin, Sakin; Bindal, Cuma (ELSEVIER SCIENCE SA, 2008)

In this study, aluminum powder with 15 mu m size and carbonyl-nickel powder with 4-7 mu m size having 99% and 99.8% purity, respectively were used in order to produce NiAl by volume combustion synthesis. The production of ...