In this study, we describe new collagen/functionalized multiwalled carbon nanotube/chitosan/hydroxyapatite (Col/f-MWCNT/CS/HA) composite scaffolds which were fabricated by freezing ( - 40 degrees C at 0.9 degrees C/min) ...

In this study, we describe new collagen/functionalized multiwalled carbon nanotube/chitosan/hydroxyapatite (Col/f-MWCNT/CS/HA) composite scaffolds which were fabricated by freezing ( - 40 degrees C at 0.9 degrees C/min) ...

In this study, hydroxyapatite coating on titanium material substrate was successfully performed by using biomimetic method. Titanium plates immersed in 1.5 SBF at pH 7.4 and 37 degrees C were analyzed at the end of the ...

Ti6Al4V plates were exposed to soaking alkali treatment resulted in Na0.23TiO2 phase on the surface before realizing biomimetic Calcium-Phosphate (CaP) coating in prepared m-5xSBF and 5xSBF solutions at 37 degrees C and ...

Ti6Al4V plates were exposed to soaking alkali treatment resulted in Na0.23TiO2 phase on the surface before realizing biomimetic Calcium-Phosphate (CaP) coating in prepared m-5xSBF and 5xSBF solutions at 37 degrees C and ...

Nano-sized hydroxyapatite (HA) particles were synthesized by sol-gel through water and ethanol based mediums of phosphoric acid (H3PO4) and calcium hydroxide (Ca(OH)(2)) at pH = 11 for different calcination time (1 h, 2 ...

In this study, some properties of biomimetic synthesized hydroxyapatite by using different sources of calcium were investigated. Biomimetic synthesis of hydroxyapatite was carried out in microwave oven using 1.5 simulated ...

In this study, some properties of biomimetic synthesized hydroxyapatite by using different sources of calcium were investigated. Biomimetic synthesis of hydroxyapatite was carried out in microwave oven using 1.5 simulated ...

This study reports on biomimetic mineralization route employing reduced graphene oxide (RGO) at different rates as a template material for biomineralization of biphasic hydroxyapatite/tricalcium phosphate (HAP/TCP). ...