dc.identifier.citation Taktak, S; Artir, R; Yilmaz, S; Bindal, C; (2004). KEY ENGINEERING MATERIALS. EURO CERAMICS VIII, PTS 1-3, 264-268, 984-981
dc.identifier.isbn 0-87849-946-6
dc.identifier.issn 1013-9826
dc.identifier.uri https://hdl.handle.net/20.500.12619/70161
dc.description.abstract The aim of this study is to investigate fracture toughness of alumina-mullite composites produced by infiltration process. Alumina-mullite composite samples were fabricated using a hydrolyzed ethyl silicate sol (TEOS) which was infiltrated as SiO2 source into alumina preforms. Infiltrated samples were cold pressed isostatically at 150 MPa at vacuum followed by presintering at 1200degreesC for one hour. Final sintering was carried out at 1650 degreesC for 4 hours. Phases formed after sintering were determined by XRD revealing alumina and mullite phases. Fracture toughness measurements were performed by using indentation technique indicating that fracture toughness of samples was increased with raising mullite content.
dc.language English
dc.publisher TRANS TECH PUBLICATIONS LTD
dc.subject Materials Science
dc.title KEY ENGINEERING MATERIALS
dc.type Proceedings Paper
dc.identifier.volume 264-268
dc.identifier.startpage 981
dc.identifier.endpage 984
dc.contributor.saüauthor Artır, Recep
dc.contributor.saüauthor Yılmaz, Saim
dc.contributor.saüauthor Bindal, Cuma
dc.contributor.saüauthor Yılmaz, Şenol
dc.relation.journal EURO CERAMICS VIII, PTS 1-3
dc.identifier.wos WOS:000223059700232
dc.contributor.author Artır, Recep
dc.contributor.author Yılmaz, Saim
dc.contributor.author Bindal, Cuma
dc.contributor.author Yılmaz, Şenol


Files in this item

Files Size Format View

There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record