Abstract:
In the present work, a nickel sulfate bath containing SiC submicron particles between 100 and 1000 nm was used as the plating electrolyte. The aim of this work is to obtain Ni-SiC metal matrix composites (MMCs) reinforced with submicron particles on steel surfaces with high hardness and wear resistance for using in anti-wear applications such as dies, tools and working parts for automobiles and vehicles. The influence of the SiC content in the electrolyte on particle distribution, microhardness and wear resistance of nano-composite coatings was studied. During the electroplating process, the proper stirring speed was also determined for sub-micron SiC deposition with Ni matrix. The Ni films were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. The depositions were controlled to obtain a specific thickness (between 50 and 200 mu m) and volume fraction of the particles in the matrix (between 0.02 and 0.10). The hardness of the coatings was measured to be 280-571 HV depending on the particle volume in the Ni matrix. The tribological behaviors of the electrodeposited SiC nanocomposite coatings sliding against an M50 steel ball (empty set 10 mm) were examined on a tribometer. All the friction and wear tests were performed without lubrication at room temperature and in the ambient air (with a relative humidity of 55-65%). The results showed that the wear resistance of the nanocomposites was approximately 2-2.2 times more than those of unreinforced Ni. (C) 2011 Elsevier B.V. All rights reserved.