In this study the abrasive wear behaviour of aliphatic polyketone (APK), polyoxymethylene (POM), ultrahigh molecular weight polyethylene (UHMWPE), polyamide 66 (PA66), and 30% glass fibre reinforced polyphenylenesulfide ...

In this study the wear volume map is obtained and considered for evaluation of the abrasive wear performance for polyamide (PA6) and PA6 composites. Polyamide composites were tailored using 25 wt.% glass bead, 20 wt.% talc ...

In this study, the effect of applied load and sliding speed on friction and wear behaviour of 25 wt% bronze filled polytetrafluoroethylene (PTFE) composite is experimentally examined and analytically analysed. Friction and ...

In present study, kinetic studies on borided AISI 5140, AISI 4340 and AISI D2 steels are reported. Steels were borided in a salt bath consisting of borax, boric acid and ferro-silicon between 1073 and 1273 K for 2, 4, 6 ...

In this study, some properties of borided perlitic ductile irons were investigated. Boronizing was realized in a salt bath and appropriate boronizing heat treatment was carried out between under atmospheric pressure. Borides ...

In this work, the friction and wear properties of Cr, V, Ti and Mo doped-niobium carbide coatings were examined. The coatings were obtained by thermo-reactive deposition/diffusion (TRD) technique on AISI 4140 steel at 1000 ...

In this investigation, the influence of test speed and applied pressure values on the friction and wear behaviour of polyamide 66 (PA 66), polyoxymethylene (POM), ultrahigh molecular weight polyethylene (UHMWPE), 30% glass ...

GGG-50, GGG-60 and GGG-80 ductile cast irons containing 0.01, 0.3 and 0.98 wt% copper, respectively, were boronized in a salt bath and then analyzed using optical microscopy, scanning electron microscopy and X-ray diffraction ...

Originality/value - The properties of the tribological properties of ductile cast irons have not explained detail in the earlier study. There are new results in this study on the tribological properties of boronized ductile ...