Abstract:
Due to today's high-frequency trainloads and wheel or rail irregularities, the railway system is more exposed to impact loading conditions. In this study, laminated carbon fiber reinforced polyurethane (L-CFRPU) products were used, with a new non-pre-stressed production process, to improve the impact damping characteristics of concrete railway sleepers. New designed LCR-6 type sleepers were compared with standard B70 type pre-stressed concrete sleepers by performing modal analysis before and after a 50 times repeated-330 kN impact loading procedure. This is the first study to compare new LCR-6 type sleepers with prestressed competitors after impact loads. According to the analysis results, FRF magnitude values decrease up to 83% lower in impacted LCR-6 type sleepers compared to impacted B70 type sleepers. After the impact loading procedure, the cracks formed in LCR6 type sleepers closed and remained below 50-mu m width, and according to the simultaneous mechanical test results, these few hairline cracks do not cause a significant mechanical capacity loss, while increasing the damping ratios by 274%. This advantage will be beneficial in extending the service life of sleepers and protecting other railway components from vibration and impact damage. Therefore, while the pre-stressed concrete sleepers have a negative course during their service life, the non-pre-stressed LCR type sleepers show a positive acceleration.